| HP Technical parametri | ||||||||
| (M) nominis diameter | (M) nominis diameter | |||||||
| Item | Unitas | Yb / T4090 Industry Latin) | HP (mensus valorem) | |||||
| CC \ CD | CDL \ D | DC \ DCC | DC \ DCC | CDL \ D | CDL \ D | |||
| Electrica resistentibus | Electrode | μqm | ≤7.0 | ≤7.5 | ≤7.5 | 5.6-6.5 | 5.8-6.7 | 5.8-6.8 |
| Papilla | ≤6.3 | ≤6.3 | ≤6.3 | 3.5-4.3 | 3.5-4.2 | 3.5-4.2 | ||
| Mole density | Electrode | G / CM³ | ≥1.60 | ≥1.60 | ≥1.60 | 1.7.-1.75 | 1.72-1.74 | 1.70-1.72 |
| Papilla | ≥1.72 | ≥1.72 | ≥1.72 | 1.80-1.82 | 1.82-1.84 | 1.82-1.85 | ||
| Flacalis fortitudinem | Electrode | MPA | ≥10.5 | ≥c10 | ≥8.5 | 12.0-15.0 | 11.0-15.0 | 10.0-12.0 |
| Papilla | ≥17.0 | ≥17.0 | ≥17.0 | 22.0-26.0 | 22.0-26.0 | 24.0-28.0 | ||
| Cte | Electrode | X ℃ | ≤2.4 | ≤2.4 | ≤2.4 | 1.7-2.0 | 1.6-2.0 | 1.6-2.0 |
| Papilla | ≤2.2 | ≤2.2 | ≤2.2 | 1.4-1.8 | 1.4-1.8 | 1.4-1.8 | ||
| Elastica modulus | Electrode | Gpa | ≤14.0 | ≤14.0 | ≤14.0 | 9.0-12.0 | 9.0-11.5 | 9.0-11.5 |
| Papilla | ≤16.0 | ≤16.0 | ≤16.0 | 14.0-16.0 | 15.0-18.0 | 15.0-18.0 | ||
| Cinis | Electrode | % | ≤0.5 | ≤0.5 | ≤0.5 | ≤0.5 | ≤0.5 | ≤0.5 |
| Papilla | ||||||||
| Nominis diameter | Cross-Sectional Area | Yt / T4090 (Industry Latin) | HP (Enterprise Latin) | |||
| Licitum current onus | Current density | Licentiosus Onus | Current density | |||
| in | mm | cm² | A | A / C² | A | A / C² |
| XIV | CCCL | CMXXXVII | 17400-24000 | 17-27 | 18270-25200 | 19-26 |
| XVI | CD | MCCLXXV | 21000-31000 | 16-24 | 22050-32550 | 17-26 |
| XVIII | CDL | MDCXXII | 25000-40000 | 15-24 | 26250-42000 | 16-26 |
| XX | D | MM | 30000-48000 | 15-24 | 31500-50400 | 16-25 |
| XXII | DL | MMCDXXVII | 34000-53000 | 14-22 | - | - |
| XXIV | DC | MMDCCCXCII | 38000-58000 | 13-21 | - | - |
| XXVIII | DCC | MMMCMXXXV | 45000-72000 | 12-19 | - | - |
| Ductu ad analysis of Electrode problems | |||||||
| Factors | Corpus fractio | Papilla fractio | Laxitas | Tip spalling | DESIGNO | Oxidatio | Consummatio |
| Nonconductor in causam | ◆ | ◆ | |||||
| Gravibus exiguo in causam | ◆ | ◆ | |||||
| Verto capacitatem nimis magna | ◆ | ◆ | ◆ | ◆ | ◆ | ◆ | |
| Tempus disparitas | ◆ | ◆ | ◆ | ◆ | ◆ | ||
| Phase gyrationis | ◆ | ◆ | ◆ | ||||
| Nimia vibrationis | ◆ | ||||||
| Clamper pressura alta vel nimis | ◆ | ◆ | ◆ | ||||
| Tectum Electrode Shot Desalignment cum Electrode | ◆ | ◆ | ◆ | ||||
| Aqua sprayed in electrodes supra tectum | △ | ||||||
| PRAEVALIDUS | △ | ||||||
| Secundarium voltage nimis | ◆ | ◆ | ◆ | ◆ | ◆ | ||
| Secundarium current nimis | ◆ | ◆ | ◆ | ◆ | ◆ | ◆ | |
| Power factor nimis | ◆ | ◆ | ◆ | ||||
| Oleum consummatio nimis | ◆ | ◆ | ◆ | ◆ | |||
| Oxygeni consummatio est princeps | ◆ | ◆ | ◆ | ◆ | |||
| Longa gap a percussoque percussoque | ◆ | ◆ | |||||
| Electrode tumping | ◆ | ◆ | |||||
| Sordida | ◆ | ◆ | |||||
| Sinelata levare plug et tensis tool | ◆ | ◆ | ◆ | ||||
| Satis iuncturam tensis | ◆ | ◆ | ◆ | ||||
| Note: △ indicat auctus perficientur. ◆ indicat decrescebat perficientur. | |||||||
High-potentia graphite electrodes produci per maxime factum de PETROLEUM Coke et acus Coke ut rudis materiae, calculus heri picem ut ligans, et factum est per calciam, batching, miscentes, et in calcinia, graphitization, et mixtura, et calcinia, graphitization, et in calculo, graphitization, et machining. Sunt Conductors quod dimittere electricity in forma arcus in electrica arcum fornacem ad calorem et conflandum in fornacem materiale. Secundum quale Indicatores, potest dividi in ordinarium graphite electrodes, altus-potentia Graphite electrodes, et ultra-princeps potentia Graphite Electrodes. Graphite electrodes sunt communiter in electrica arcum Furnaces (quia Steelmaking) et demerguntur Arcus Furnaces (nam producendo Ferroallowys, pure Silicon, phosphoro, calcium carbide, etc.). Et resistentia Furnorum, ut Graphitization Furnorum ad producendo graphite electrodes, vitrum liquescens Furnorum et electrica fornaces ad adamantino harenae. Potest processionaliter secundum elit requisita, maxime propter arcus fornacem Steelmaking.
Product commodum
(I) De augendae complexionem fingunt geometria et diversitas ex productum applications duci ad superiora requisita pro missionem accurate de scintilla machinarum. Commoda Graphite Electrodes sunt facile processus, alta officia machinens remotionem rate et humilis graphite damnum. Ideo quaedam coetus fundatur scintilla apparatus customers deserta aeris electrodes et switched ad graphite electrodes. Praeterea, quidam speciali informibus electrodes non est aeris, sed graphite est facillimus ad formam et aeris electrodes sunt graviora, faciens ea inconvenienter ad processui magna electrodes. Hae factores duci ad aliquid coetus fundatur scintilla apparatus customers per Graphite Electrodes.
(II) graphite electrodes sunt facillimus ut processus et a significantly citius processui celeritate quam aeris electrodes. Exempli gratia, uti Milling technology ad processus graphite, eius processus celeritas est 2-3 velocius quam alius metallum processus et non eget additional manual processus, cum aeris Electrodes eget manual molere. Similiter, si summus celeritas graphite machining centers sunt ad fabricare electrodes, celeritas erit citius, efficientiam erit altior, et non erit pulvis forsit. In his machining processibus, eligendo tools cum oportet duritiam et graphite potest reducere tool gerunt et aeris electrode damnum. Si comparet milling tempus Graphite electrodes et aeris electrodes, Graphite electrodes sunt LXVII% citius, quam aeris electrodes. In generali, in missionem machining, utendo graphite electrodes est LVIII% citius quam usura aeris electrodes. Et hoc modo, processui tempus est significantly reducitur, cum etiam reducing vestibulum costs.
(III) De Design of Graphite Electrodes est aliud ex traditional aeris electrodes. Multi fingunt factories plerumque habent diversas reservare pro aspera et praecisione machining de aeris electrodes, dum graphite electrodes uti fere eadem Subsidium moles, quod reducit frequency de Cad / Cam et apparatus processui. Hoc solum satis est valde amplio accurate de fingere cavitatis.
Processing formas de Graphite Materials
Sunt tres principes formas dispensando graphite electrodes: pressurized vibrationem modum, cnc automatic formatam modum, et mechanica processus modum.
Graphite materiae potest processionaliter uti modi ut conversus, milling, EXERCITATIO et molere. Praeterea, graphite materiae sunt prone fugere cinere per mechanica processus, quae adversa effectus in dispensando apparatu et operators.
Processing formas de Graphite Materials
(I) dum productionem cycle. Productio exolvuntur Ordinarius Power Graphite Electrodes est de XLV diebus, et productio cycle of ultra-altus potentia Graphite electrodes plus quam LXX diebus. Tamen, ad productionem cycle of Graphite Electrode compagibus qui requirere multa impregnations longior.
(II) princeps industria consummatio. I ton Ordinarius Power Graphite Electrodes requirit circiter (VI) KW · h de electrica industria, millia cubicae metris de Gas seu naturalis Gas et circiter I ton of metallurgical Coke particulas et pulveris.
(III) Sunt plures productio processibus. Productio processus includit rudis materia calciam, adtritis et stridor, batching, bulding, shaping, torrendo, impregnation, graphitization, et mechanica processus. Eius productio requirit multa specialized mechanica apparatu et vstrinat cum speciali structuris, et constructione investment est magna, cum diu elit payback tempus.
(IV) Quaedam quantitate pulveris et nocivis gasorum generatae per productionem processus, et necesse est ut comprehensive evacuatione et pulvis reductionem mensuras superiores et environmental tutela mensuras superiores nocivis gases.
(V) requiritur carbonaceous rudis materiae ad productionem, ut PETROLEUM Coke et Coal TORPUS picem, sunt per-products of conflans et carbonibus eget. Et qualis et stabilitatem de rudis materiae sunt difficile ad plene praestare, praesertim acus Coke, modified electrode picem, et speciali impraegnating agente pice cum humilis quinta insolible contentus in altum potentia et ultra-altus potentia Graphite Electrode productio. Est urgente pro Sinis scriptor PETROLEUM et Coal Chemical Processing conatibus adiungere momenti ad ac actively cooperatur.
Productionem applicationem
(I) propter electrica arcus Steelmaking Furnas
(II) usus ad metalla electrica Furnorum
(III) usus est resistentia fornaces
(IV) usus est parat irregulares Graphite Products
Turba introductio
Handan tuoda Novum Material Technology Co., Ltd. est professional graphite elit dedicavit ad investigationem et progressionem, dispensando, vestibulum, et Sales de Graphite products. In comitatu habet fortis oeconomica fortitudinem et provectus technica firmamentum, et habet developed Graphite products cum domesticis cash technology campester, providing customers cum integrated officia ex materia electionem consilium et dispensando. Et uber est late in variis agris, comprehendo in electronic semiconductor industria, mechanica processus industria, aerospace industria, et eget industria. Nos providere customers cum summus qualitas products et sinceram servicia, continuously discere et explorandum technology, et statutum cooperantem relationes cum multyenterprises.